Manufacturing of Kevlar/Polyester Composite by Resin Transfer Moulding using Conventional and Microwave Heating

Kevlar/Polyester Composite Manufacturing

Abstract

Microwave heating was incorporated into the resin transfer moulding technique. Polytetrafluoroethylene (PTFE) mould was used to cure the composite panel. Through the use of microwave heating, the mechanical and physical properties of produced Kevlar fibre/polyester composites were compared to those manufactured by conventional resin transfer moulding. The flexural modulus and flexural strength of 6-ply conventionally cured composites was 45% and 9% higher than the flexural modulus and flexural strength of 6-ply microwaved cured composites, respectively. However, 19% increase in interlaminar shear strength (ILSS) and 2% increase in compressive strength was observed in 6-ply microwave cured composites. This enhancement in ILSS and compressive strength is attributed to the better interfacial bonding of polyester resin with Kevlar fibres in microwaved cured composite, which was also confirmed via electron microscopy scanning. Furthermore, the microwave cured composite yielded maximum void contents (3%).